What is H13 tool steel?

What is H13 tool steel?

H13 is a hot-work tool steel, meaning it holds its strength and hardness up to a higher working temperature than most tool steels. We are launching H13 Tool Steel to give people the ability to print high-strength, high-temperature parts.

What is the material composition for H13?

H13 is a hot work tool steel that has good resistance to thermal fatigue, erosion and wear, and is widely used for making molds and dies. The H13 powder used for laser consolidation contains 0.42% C, 5.04% Cr, 1.33% Mo, 1.06% V, and 0.88% Si.

What is S7 tool steel used for?

S7 tool steel properties make it a preferred type for riveting, notching, blanking cold forming and bending dies; bull riveters, concrete breakers, dowels, drill plates and hubs.

What is SKD11 equivalent to?

GB Cr12MoV
Equivalent Grades: GB Cr12MoV, JIS SKD11, AISI/SAE D3, DIN 2X165CrMoV12. SKD11 is the tool steel, die steel, and high carbon steel possessing high hardness, strength and wear resistance. Its surface is grinded precisely. It is often used for the stamping dies, plastic molds, and so on.

How hard can you get H13?

For hot work applications, H13 is used in the hardness range of HRC 38 to 48. The usual hardness range for die casting dies is HRC 44 to 48 requiring a temper at approximately 1100°F. For improved shock resistance, the steel is often tempered at temperatures approaching 1150°F, resulting in hardnesses of HRC 40 to 44.

What is the difference between H11 and H13 steel?

If we compare between H11 and H13, H11 tool steel consists of less vanadium than the commonly used H13 hot work tool steel. This gives H11 steels the higher toughness, with some reduction in wear resistance and tamper resistance.

How is H13 tool steel made?

The common smelting methods of AISI H13 tool steel include electric furnace smelting + electroslag remelting, ladle refining(LF) and electric furnace smelting + vacuum degassing(VD).

How hard can H13 get?

How do you heat treat h13?

H-13 should always be annealed after forging. Heat slowly to 1550°-1650°F, hold until entire mass is heated through, and cool slowly in the furnace (40F per hour) to about 1000°F, after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.

Is SKD11 stainless steel?

2379 / SKD11 Steel is Chrome steel 12% with very high resistance against abrasive and adhesive wear due to a high volume of hard carbides in the steel matrix, good toughness, very good dimensional stability, high compressive strength, very good base material for PVD/CVD coating as well as nitriding due to its secondary …

What material is SKD11?

SKD11 Tool Steel is a high- carbon and high- chromium alloy tool steel. It has good wear resistance and size ability after heat treatment and is suitable for making long-life high-precision cold-work dies. SKD11 Tool Steel of Applications: 1) Making knife-edge mold, scissors, circular saw blades, metal stamping mold.

What is H13 tool steel used for?

H13 Tool Steel is a versatile chromium-molybdenum hot work steel that is widely used in hot work and cold work tooling applications. The hot hardness (hot strength) of H13 resists thermal fatigue cracking which occurs as a result of cyclic heating and cooling cycles in hot work tooling applications. Because of its excellent combination of high

What is the composition of H13 die steel?

All the samples used in the current study are H13 tool steel (commercial name: ORVAR 2 Microdized), a typical die steel used for hot extrusion dies with the following composition (%wt): 0.39% C, 1% Si, 0.4% Mn, 5.3% Cr, 1.9% Mo, 0.9% V, and balance Fe.

What is AISI H13 steel?

J.C. Outeiro, in Mechanics of Materials in Modern Manufacturing Methods and Processing Techniques, 2020 AISI H13 tool steel is characterized by good resistance to thermal softening, high hardenability, high strength, and high toughness.

What is H13 die casting used for?

Designed to retain hardness at elevated temperatures, and to withstand the effects of alternate heating and cooling, H13 is used extensively in aluminum extrusion, aluminum die casting, and forging die applications. It’s exceptional toughness and inherent resiliency have also made this a popular material for die casting in the cold heading field.